Process for thickening thermoset resin molding compound compositions

ABSTRACT

This invention relates to a process for making a thickened thermoset resin composition, comprising: mixing 
     (A) a carboxylic acid containing thermoset resin composition; and 
     (B) at least one compound represented by the formula ##STR1## wherein in Formula (B-I): R 1 , R 2 , R 3  and R 4  are independently hydrogen or methyl; R 5  is hydrogen, a hydrocarbon group or a substituted hydrocarbon group, the substituents on said substituted hydrocarbon group comprising oxygen and/or nitrogen; and n is at least 1.

TECHNICAL FIELD

This invention relates to a process for thickening thermoset resin molding compound compositions. More particularly, this invention relates to a process for thickening thermoset resin molding compound compositions using an aziridine thickening agent.

BACKGROUND OF THE INVENTION

There are a number of known methods for thickening thermoset polyester resin compositions. One of these methods involves the use of inorganic oxides, such as magnesium oxide, to thicken unsaturated polyester resins blended with styrene. Another method involves the coreaction of polyisocyanates with hydroxyl groups contained within the polyester resin or added as a coreactant to form urethane linkages. A third method involves the trimerization of polyisocyanates with the use of a catalyst. A problem with the metal oxide or hydroxide prior art methods is that an inherently stable viscosity plateau is not achieved, and the molding compounds thickened by these techniques have relatively short shelf lives and do not remain soft and pliable for sufficiently long periods of time. A problem with polyisocyanate prior art methods is that the polyisocyanates are sensitive to water and to acid functional groups found in the molecular structures of many resins. These problems are overcome by the present invention which involves the use of an aziridine compound as a thickening agent.

SUMMARY OF THE INVENTION

This invention relates to a process for making a thickened thermoset resin composition comprising, mixing:

(A) a carboxylic acid and optionally amine acceptor containing thermoset resin composition; and

(B) at least one compound represented by the formula ##STR2## wherein in Formula (B-I): R¹, R², R³ and R⁴ are independently hydrogen or methyl; R⁵ is hydrogen, a hydrocarbon group or a substituted hydrocarbon group, the substituents on said substituted hydrocarbon group comprising oxygen and/or nitrogen; and n is at least 1. This process is useful in making improved sheet molding compounds, bulk molding compounds, thick molding compounds, and the like.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a schematic representation of a sheet molding compound machine for making sheet molding compounds using thickened thermoset resin compositions made by the inventive process.

DESCRIPTION OF THE PREFERRED EMBODIMENTS

The thermoset resin composition (A) may comprise: (i) an acid functionalized thermoset resin containing at least one carboxylic acid group in its molecular structure; (ii) a mixture of a thermoset resin, and at least one carboxylic acid; or (iii) a mixture of an acid functionalized thermoset resin containing at least one carboxylic acid group in its molecular structure, and at least one carboxylic acid.

The carboxylic acid group may be derived from an anhydride group. For example, anhydride groups may be hydrolyzed to form acid groups. The thermoset resin composition (A) may optionally comprise an amine acceptor group. An amine acceptor group is a functional group capable of being reactive with an amine, especially a secondary amine. Examples of the amine acceptor group include anhydride groups, epoxy groups and isocyanate groups. If an anhydride group is present, and if it remains unconverted, then it may act as an amine acceptor group.

In one embodiment, the carboxylic acid in (ii) or (iii) is an oligomer or a polymer having at least one carboxylic acid group in its molecular structure. The thermoset resin can be any thermoset resin, examples of which include unsaturated polyesters, vinyl esters, isocyanurate vinyl esters, epoxies, poly(ester-imides), bisphenol A fumaric types, cyanate esters, epoxy vinyl esters, phenolics, acrylics, and mixtures of two or more thereof. In one embodiment, the acid functionalized resin is an unsaturated polyester, poly(ester-imide), novolac vinyl ester, or mixture of two or more thereof.

The unsaturated polyesters are condensation polymers made by the condensation of unsaturated polybasic acids and anhydrides, such as dibasic acids or anhydrides, with polyols, such as dihydroxy or trihydroxy compounds. The polyesters may include in the polymeric chain, varying proportions of other saturated or aromatic dibasic acids and anhydrides which are not subject to crosslinking. The particular non-crosslinking components and their properties will depend upon the desired properties of the final products.

Examples of unsaturated polybasic acids or anhydrides which are utilized in the formation of the polyester resins include maleic acid, fumaric acid, itaconic acid, tetrahydrophthalic acid, or the anhydrides of any of the foregoing. Examples of saturated aliphatic polycarboxylic acids include adipic and succinic acids, and examples of aromatic polycarboxylic acids include phthalic acid, isophthalic acid, terephthalic acid and halogenated derivatives such as tetrachlorophthalic acid and anhydride.

Examples of polyols include dihydroxy and trihydroxy compounds which in turn include ethylene glycol, propylene glycol, 1,2-butanediol, 1,3-butanediol, 1,4-butanediol, diethylene glycol, dipropylene glycol, glycerol, neopentyl glycol, and reaction products of alkylene oxides with, for example, 2,2'-bis(4-hydroxy phenylene)propane, (Bis-phenol A).

The polyesters are prepared by reacting the one or more polybasic acids or anhydrides with the polyols (di- or tri-hydroxy compounds) in approximately equal proportions. Examples of such polyesters include: maleic anhydride and propylene glycol (1:1 molar ratio); isophthalic acid, maleic anhydride and propylene glycol (1:2:3 and 1:1:2 molar ratios); and adipic acid, maleic anhydride and propylene glycol (1:2:3 molar ratio). The degree of polymerization of polyester resins is conveniently measured with respect to the acid end groups on a solids basis or dissolved in styrene. One gram of the polyester resin is titrated with potassium hydroxide, and the number of milligrams of potassium hydroxide necessary to neutralize the gram of polyester is called the acid number. In one embodiment of this invention, the acid number of the polyester resin in styrene solution is from about 2 to about 50, and in one embodiment about 12 to about 24.

A wide variety of unsaturated polyester resins can be used. These include the polyester resin-styrene monomer solutions marketed by: Aristech Chemical Corporation under the trade designations MR, LB, LAM, P, and E, specific examples being MR 13038 which is identified as an unsaturated polyester resin-styrene monomer solution having a styrene monomer content of about 30%, MR 13017 which is identified as an isophthalate type unsaturated polyester resin-styrene monomer solution having a styrene monomer content of about 32.5%, and MR 14017 which is identified as an isophthalate type unsaturated polyester resin-styrene monomer solution having a styrene monomer content of about 31.5%; and DSM Resins under the trade designation Daron XP 21-102 which is identified as a polyester-imide dissolved in styrene monomer, the styrene monomer content of about 32-34% by weight.

The acid-functionalized unsaturated polyester resins that can be used include: Polylite 31-610-00, a product of Reichhold identified as a propylene glycol-isophthalate, maleate type unsaturated polyester dissolved in styrene monomer, the styrene monomer content being a maximum of about 32% by weight; Polylite 31-615-20, a product of Reichhold identified as propylene glycol-maleate type unsaturated polyester resin dissolved in styrene monomer, the styrene monomer content being a maximum of about 35% by weight; E-903, a product of Alpha Owens Corning identified as a dicyclopentadiene modified propylene glycol-maleate type unsaturated polyester dissolved in styrene monomer, the styrene monomer content of about 26.5-31.5% by weight; and E-4381, a product of Alpha Owens Corning identified as a modified polyester resin dissolved in styrene monomer, the styrene monomer maximum content of about 37% by weight.

The isocyanurate vinyl ester resins that can be used include Atlac® ITP® 31-632-00, a product of Reichhold identified as an isocyanurate vinyl ester resin dissolved in styrene monomer, the styrene monomer content of about 47-52% by weight; and 7568-44-3, a product of Reichhold identified as an isocyanurate vinyl ester containing a proprietary polyol and being dissolved in styrene monomer, the styrene monomer content being a maximum of 35% by weight.

Bisphenol A fumaric type resins useful include Atlac® 382-ES, a product of Reichhold, identified as a solid propoxylated bisphenol A fumaric polyester resin; and Atlac® 382-ES HMW, a product of Reichhold, also identified as a solid propoxylated bisphenol A fumaric polyester resin.

The cyanate ester resins that are useful include AroCy L-10, a product of Ciba Geigy identified as a bisphenol E dicyanate ester.

The epoxy resins that are useful include Epon 828, a product of Shell identified as a bisphenol A epoxy resin.

The vinyl ester resins that can be used are the reaction products of epoxy resins and monofunctional ethylenically unsaturated carboxylic acids. They may be represented by the formula ##STR3## where R¹ is H or CH₃, and R² is an epoxy resin, examples of the latter including epoxylated bisphenol A-epichlorohydrin and epoxylated phenolformaldehyde novolac. These resins can be made by reacting an epoxy resin with an ethylenically unsaturated carboxylic acid. The epoxy resins that can be used include diglycidyl ether of bisphenol A and higher homologues thereof, the diglycidyl ether of tetrabromobisphenol A, epoxylated phenolformaldehyde novolac, and polypropylene oxide diepoxide. The acids that can be used include acrylic and methacrylic acid. The acid-epoxide reaction can be catalyzed by tertiary amines, phosphines, alkalis, or onium salts. Examples of commercially available vinyl ester resins that can be used include Derakane 780, a product of Dow identified as a solution of an acid functionalized novolac vinyl ester resin dissolved in styrene monomer, the styrene monomer content being about 30-40% by weight and Derakane 470-36, a product of Dow identified as an epoxy novolac vinyl ester resin dissolved in styrene monomer, the styrene monomer content of about 36% by weight. The epoxy vinyl esters that can be used include Derakane 411-45, a product of Dow identified as a solution of an epoxy vinyl ester resin dissolved in monomeric styrene, the content of the monomeric styrene of about 45% by weight.

The carboxylic acid or anhydride can be any organic carboxylic acid or anhydride. Examples include acrylic acid, methacrylic acid, maleic acid or anhydride, succinic anhydride, fumaric acid, phthalic acid or anhydride, isophthalic acid, terephthalic acid, adipic acid, polyadipic anhydride, fatty acids, and mixtures of two or more thereof.

The carboxylic acid or anhydride containing oligomer or polymer can be any oligomeric or polymeric material having in its molecular structure at least one carboxylic acid or anhydride group. Examples of the oligomers and polymers that can be used include polybutadiene, copolymers of butadiene and acrylonitrile, styrene maleic anhydride copolymers and various olefin maleic anhydride copolymers. Examples of commercially available materials that can be used include: the carboxyl terminated butadiene acrylonitrile liquid copolymers supplied by BFGoodrich under the tradename Hycar, specific examples including Hycar 1300X8, Hycar 1300X9, Hycar 1300X13, Hycar 1300X18, and Hycar 1300X31; and the polybutadiene polymers adducted with maleic anhydride supplied by Ricon Resins under the trade designations Ricon 131/MA-5, Ricon 131/MA-10, Ricon 131/MA-12 and Ricon 131/MA-17. An example of a commercially available carboxyl terminated polybutadiene is Hycar 2000X162 supplied by BFGoodrich.

Isocyanate group containing compounds useful as an amine acceptor group include PCA 6-3, a product of Polyurethane Specialties identified as an MDI based polyether prepolymer.

The compounds (B) can be any aziridine compound represented by the formula ##STR4## wherein in Formula (B-I): R¹, R², R³ and R⁴ are independently hydrogen or methyl; R⁵ is hydrogen, a hydrocarbon group or a substituted hydrocarbon group, the substituents on the hydrocarbon groups comprising oxygen and/or nitrogen atoms; and n is at least 1, and in one embodiment n is in the range of 2 to about 4, and in one embodiment 2 to about 3, and in one embodiment 3 to about 4. In one embodiment, R¹, R², R³ and R⁴ are each hydrogen. In one embodiment, R¹ is methyl, and R², R³ and R⁴ are hydrogen. R⁵ can have from about 1 to about 10,000 carbon atoms, and in one embodiment from about 1 to about 500 carbon atoms. In one embodiment, these compounds are represented by the formula ##STR5## wherein in Formula (B-II): R¹ is an alkylene group, which in one embodiment contains 1 to about 10 carbon atoms; R² is a hydrocarbyl group or a substituted hydrocarbyl group, which in one embodiment contains 1 to about 10,000 carbon atoms, and in one embodiment, 1 to about 500; and R⁵ is a hydrogen or methyl group. In one embodiment, these compounds are represented by the formula ##STR6## wherein in Formula (B-III): R¹ and R² are alkylene groups, which in one embodiment contains 1 to about 10 carbon atoms; R³ is hydrogen, a hydrocarbyl group or a substituted hydrocarbyl group, which in one embodiment contains 1 to about 500 carbon atoms, and in one embodiment 1 to about 50 carbon atoms; and n is a number in the range of 1 to 4; and R⁵ is a hydrogen or methyl group. In one embodiment, these compounds are represented by the formula ##STR7## wherein in Formula (B-IV) R¹ is --C₂ H₅ or --CH₂ OH and R⁵ is a hydrogen or methyl group. Examples of aziridines compounds that can be used include the polyfunctional aziridines supplied by EIT, Inc. under the trade designation XAMA, including XAMA-2, which is identified as trimethylol propane-tris (beta-(N-aziridinyl) proprionate), and XAMA-7, which is identified as pentaerythritol-tris-(beta-(aziridinyl) propionate); under the trade designation Ionac® including PFAZ-322, a product of Sybron Chemicals, identified as a trifunctional aziridine; and including CX-100, a product of Zeneca Resins, identified as a polyfunctional aziridine.

In the formulae above, in preferred embodiments, n is at least 2 when an amine acceptor is not used. In another preferred embodiment, n is at least 1 when an amine acceptor is used, especially when the amine acceptor has a functionality of at least 2. In another preferred embodiment, n plus the number of the amine acceptor functionality is at least about 2 and more preferably at least about 3.

The molar ratio of carboxylic acid group in the resin composition (A) to aziridine groups (i.e., N-) in (B) is generally from about 0.05 to about 20, and in one embodiment about 0.25 to about 4. In a preferred embodiment, the molar ratio of carboxylic acid group in the resin composition (A) to aziridine groups in (B) is at least about 0.5 to about 1.

In one embodiment, a supplemental thickening agent (C) is used in combination with the aziridine (B). This supplemental thickening agent can be an inorganic metal oxide or hydroxide, the metal being selected from the group consisting of Mg, Ca, Zn, and mixtures of two or more thereof. In preferred embodiments, Mg, Ca, and Zn oxides and Mg and Ca hydroxides are used. In one embodiment, the ratio of aziridine groups (i.e., N-) in (B) to metal atoms in (C) is from about 0.01 to about 100, and in one embodiment about 0.1 to about 10. Specific examples include PG-9033, a product of Plasticolors, which is identified as a MgO dispersion and PG-91146, also a product of Plasticolors, which is identified as a Mg(OH)₂ dispersion.

In one embodiment, the resin composition (A) includes a free radical initiator capable of generating free radicals that can initiate crosslinking between the thermoset resin but does not cause any significant crosslinking at low temperatures. In other words, the polymerization initiators must be such that they are sufficiently stable at the temperatures at which the resin compositions are formed so that they do not prematurely crosslink and become thermoset. In one embodiment, the polymerization initiators are chosen from materials which contain either a peroxide group or an azo group. Examples of useful peroxide compounds include t-butyl perbenzoate, t-butyl peroctoate, benzoyl peroxide, t-butyl hydroperoxide, succinic acid peroxide, cumene hydroperoxide and dibenzoyl peroxide. Examples of useful azo compounds include azobisisobutyronitrile and t-butylazoisobutyronitrile. Examples of commercially available initiators that can be used include: Vazo 64, a product of DuPont identified as azobisisobutyronitrile; Trigonox 29-B75, a product of Akzo identified as a mixture of 1,1-di(tert-butyl peroxy)-3,3,5-trimethylcyclohexane and dibutyl phthalate; and Trigonox C, a product of Akzo identified as tert-butyl peroxybenzoate. Generally, the concentration of initiator in the resin composition (A) is up to about 5% by weight, and in one embodiment from about 0.1% to about 5% by weight, and in one embodiment about 0.2% to about 1% by weight.

In order to avoid premature polymerization of the polymerizable materials used in the resin composition (A), a small amount of a polymerization inhibitor can be used. Examples of such inhibitors include hydroquinone, tertiary butyl catechol, methyl ether of hydroquinone, and the like. Examples of commercially available inhibitors that can be used are those available from Plasticolors under the trade designations: SP-91029, which is identified as a mixture of 2,6-di-tert-butyl-p-cresol (25%) and vinyl toluene (75%); SP-9073, which is identified as a mixture of diethylene glycol (85%) and toluhydroquinone (15%); and SP-9139, which is identified as a mixture of dialkyl phthalate (95%) and p-benzoquinone (5%). These inhibitors can be employed in the resin compositions at concentrations up to about 1% by weight, and in one embodiment about 0.01% to about 0.2% by weight.

Wetting agents that can be used include phosphated polyesters. Examples of commercially available wetting agents that can be used include: BYK-W995 and BYK-W996, which are products of BYK-Chemie USA identified as solutions of saturated polyesters with acidic groups. These wetting agents can be employed in the resin compositions at concentrations of up to about 2% by weight, and in one embodiment about 0.5% to about 1% by weight.

Antifoam agents can be used. Typical antifoam agents include the commercially available silicone antifoam agents. Examples of commercially available antifoam agents that can be used include AF9000, a product of General Electric identified as a silicone fluid containing dimethylpolysiloxane. These antifoam agents can be employed in the resin compositions at concentrations of up to about 0.1% by weight, and in one embodiment about 0.001% to about 0.01% by weight.

Other ingredients which may be used include one or more of the following: fillers, fibrous reinforcing materials, pigments, mold release agents and thermoplastic polymeric materials.

Fillers are added as extenders to impart such properties as reduction in shrinkage and tendency to crack during curing. Fillers also tend to improve stiffness and heat resistance in molded articles. Examples of fillers that can be used include alumina trihydrate, calcium carbonate, clays, calcium silicate, silica, talcs, mica, barytes, dolomite, solid or hollow glass spheres of various densities. A commercially available filler that can be used is Camel-Wite, which is a product of Genstar Stone Products Co. identified as limestone dust (calcium carbonate).

The particular filler chosen may be dependent upon the cost of such filler, the effect of the filler on mix viscosity and flow properties, or the effect that the filler has on properties such as shrinkage, surface smoothness, chemical resistance, relative weight, flammability and/or the electrical characteristics of the cured molded article. The amounts of filler that is used may vary up to about 70% by weight, and in one embodiment from about 10% to about 50% by weight. The amount preferred for any particular formulation can be determined readily by one skilled in the art. Useful fillers generally will have an average particle size of from about 0.3 to about 50 microns, and in one embodiment about 1 to about 12 microns.

Fibrous reinforcing materials can be added for the purpose of imparting strength and other desirable physical properties to the cured products formed therefrom. Examples of fibrous reinforcements that can be utilized include glass fibers, asbestos, carbon fibers and polyester fibers, and natural organic fibers such as cotton and sisal. Useful fibrous reinforcements include glass fibers which are available in a variety of forms including, for example, mats of chopped or continuous strands of glass, glass fabrics, chopped glass and chopped glass strands and blends thereof. Preferred fibrous reinforcing materials include 0.5, 1 and 2 inch glass fibers.

The amount of fibrous reinforcing material that is used can be varied over a wide range including amounts of up to about 75% by weight, although smaller amounts will be required if any of the above-described fillers are included in the formulation. The amount of fibrous reinforcing material can vary from about 5% to about 65% by weight, and in one embodiment from about 10% to about 35% by weight. In specific embodiments, the preferable amount of fibrous reinforcing material for BMC materials is from about 10% to about 20% by weight, and the preferable amount of fibrous reinforcing material for SMC materials is from about 20% to about 35% by weight. The amount of fibrous reinforcing material to be utilized in any particular formulation depends upon the desired end use and can be determined readily by one skilled in the art.

Mold release agents also can be included and these are typically zinc, calcium, magnesium or lithium salts of fatty acids. Specific examples of mold release agents include zinc stearate, calcium stearate, magnesium stearate, lithium stearate, calcium oleate, zinc palmitate, etc. A commercially available mold release agent that can be used is Synpro Zinc Stearate Type ABG, which is a product of Synthetic Products Co. identified as zinc stearate. These mold release agents can be included in the inventive compositions at concentrations of up to about 5% by weight, and in one embodiment from about 1% to about 2% by weight.

Pigments also can be included in the inventive compositions. Typical examples of pigments include carbon blacks, iron oxides, titanium dioxide and phthalocyanines. The pigment can be dispersed into the inventive compositions as dry pigment powders or pre-dispersed forms in non-reactive carriers.

Thermoplastic polymeric materials which reduce the shrinkage of the inventive compositions during molding can also be included. These thermoplastic materials can be used to produce molded articles having surfaces of improved smoothness. Examples of useful thermoplastic polymers include homopolymers of ethylene, styrene, vinyl toluene, vinyl acetate, alkyl methacrylates and alkyl acrylates. Additional examples of thermoplastic polymers are copolymers of: vinyl chloride and vinyl acetate; vinyl acetate and acrylic or methacrylic acid; styrene and acrylonitrile; methyl methacrylate and alkyl esters of acrylic acid; methyl methacrylate and styrene; and methyl methacrylate and acrylamide. An additional example is polyurethane. Examples of commercially available polymers that can be used include: Neulon Polyester Modifier T-Plus, a product of Union Carbide identified as polyvinyl acetate-ester epoxide polymer dissolved in styrene monomer; LP-40A, a product of Union Carbide identified as a polyvinyl acetate copolymer dissolved in styrene monomer; LP-90, a product of Union Carbide identified as a polyvinyl acetate dissolved in styrene monomer; Kraton G1701, a product of Shell identified as a styrene-ethylene/propylene diblock and/or block copolymer; Finaprene 401, a product of Fina Oil and Chemical Company identified as a styrene/butadiene/styrene block copolymer; RP-700, a product of Owens Corning identified as a polymethyl methacrylate; MD-9520, a product of Chevron identified as polystyrene; and Uralloy LP-2035, a product of Ashland Chemical identified as a styrene solution of polyurethane. Up to about 15% by weight of a thermoplastic polymer can be included in the resin compositions.

The thermoset compositions of the invention are made by first preparing a composition comprising all of the ingredients for the composition, but for the fillers, fibrous reinforcing materials and the aziridine (B) and any supplemental thickening agent (C) that is to be used. This composition is prepared by first blending together the thermoset resin composition (A), and any polymerization initiators accelerators, inhibitors, mold release agents, pigments or thermoplastic polymeric materials that may be desired, using a high shear mixer. Any filler material that is to be used is then added, and the high shear mixing is continued until an adequate dispersion of all of the filler is achieved. The aziridine (B) and, if used, supplemental thickening agent (C) is then added and the mixture is mixed to form a thermoset resin paste composition. In one embodiment, the paste is then combined with any fibrous reinforcing materials that are to be used using a sheet molding compound machine of the type illustrated in FIG. 1 to form a sheet molding compound, or using a mixer to produce a bulk molding compound.

High shear mixers that can be used include Banbury mixers, cowels disperser, two roll mills, high shear compound screw extruders and similar mixers. Generally, this type of mixing results in a significant increase in the temperature of the material being mixed, and this temperature must be maintained below the critical temperatures which would result in decomposition of the polymerization initiators which would cause premature polymerization of the inventive compositions.

Sheet molding compounds are made using, for example, a sheet molding compound machine of the type illustrated in FIG. 1. Referring to FIG. 1, the sheet molding paste-like composition ("paste") is fed to the two doctor boxes. A carrier film, which can be, for example, polyethylene, nylon, and the like, is advanced past each doctor box on a conveyor belt, and a layer of paste is deposited on each carrier film. Chopped fiber strand (e.g., fiberglass) is deposited onto one layer of paste, and the other layer of paste is placed over the first layer to form a composite structure comprising the two carrier films on the outside and the paste and chopped fiber strand sandwiched in between. The composite structure is advanced through a compactor comprising a series of reduction rollers to form the inventive sheet molding compound which, in one embodiment, is in the form of a compact flat reinforced resin sheet.

The following examples illustrate the invention. Unless otherwise indicated, in the following examples as well as throughout the entire specification and in the appended claims, all parts and percentages are by weight, and all temperatures are in degrees Celsius.

EXAMPLES

Examples 1-39 and 46-54 are examples of sheet molding compounds within the scope of the invention. Examples 40-45 are examples of bulk molding compounds within the scope of the invention. These compounds are prepared using the components listed in the following Tables I-XIII by first adding all of the components except the fillers, glass fibers and the aziridine compound and supplemental thickening agents, if any, to a vessel in the order listed, then blending the resulting mixture with a high shear cowles blade mixer until the mixture is mixed. The fillers and/or glass fibers are added and the composition is mixed until the temperature increases to 80° F.-115° F. The aziridine compound and supplemental thickening agents, if any, are added, and the mixture is mixed for one minute, the resulting product being a paste-like composition. The paste is placed in the doctor boxes of a sheet molding compound machine of the type illustrated in FIG. 1 to be spread on a carrier film to produce sheet molding compounds (Examples 1-39 and 46-54), or the paste is combined with the glass fibers in a mixer to produce bulk molding compounds (Examples 40-45). Samples of the molding compounds are taken and these samples are tested for various properties such as apparent viscosity as a function of shear rate with the results being indicated in the tables.

Apparent viscosity data is generated using the Premix Processability Tester, Model PPT 1000, which evaluates squeeze flow characteristics of the molding compounds. This apparatus is a rheological instrument designed for testing sheet molding compound samples in a compression molding geometry at compression molding shear rates. The basic components of the apparatus include a load cell, a one piece cross head, hydraulic pump unit, heated platens, hardware controller and a personal computer. The tests consist of monitoring the stress as the sample is squeezed between the two platens. The load cell is located above the stationary upper platen while the lower platen moves toward it at a controlled constant velocity to a predetermined percent strain. At that point the piston is instantaneously stopped and held at a constant displacement while stress relaxation occurs. The raw data is separated into two parts representing stress build and stress relaxation. There are three regions or stages of interest in the stress build part. The first stage, where stress build is slow, is due to compaction of the material. The second stage, where stress rises quickly, is due to transient material deformation. The third stage, which follows a yield, is the steady state flow region from which apparent viscosities can be calculated.

The samples are tested using the PPT 1000 tester at 70° F. The controller and computer are turned on and the following test parameters are set:

(a) closure speed: 2 mm/sec.

(b) 0% precompression

(c) 100 KN full scale

Four plies of the 3.5-inch squares are placed between the platens, and the tests are conducted in triplicate to produce the averaged results indicated in the tables.

Mechanical properties were obtained from samples aged five days and weighing between about 500 and 650 grams. Compounds were placed in a mold at 300° F. for 2 minutes at 1,000 psi, although these parameters are not limiting in any way. The same parameters are used in the examples in order to evaluate the effects of different components on the properties of the resultant products. Tensile properties were obtained according to ASTM procedure D-638 and flexural properties were obtained according to ASTM procedure D-790.

The tables represent various examples of the present invention in addition to a number of comparative examples which do not contain an aziridine compound. Various properties are reported in the tables. Blanks indicate that data is unavailable.

Tables 1 and 2 illustrate various embodiments of the present invention.

Table 3 illustrates a low 10 minute paste viscosity obtainable by the present invention. A low paste viscosity promotes glass wet-out.

Table 4 illustrates the ability to rapidly attain a stable plateau viscosity. Practically no apparent viscosity change is observable over a 2 to 30 day period. A rapidly attained stable plateau viscosity contributes to an extended window for compound molding. The comparative examples show a rise in apparent viscosity over time.

Tables 5 and 6 generally illustrate the use of various polyester resins as component (A).

Table 7 illustrates the use of acid-containing and other coreactants for component (A).

Table 8 illustrates the use of non-acid, isocyanurate resins with acid functionalized resins and/or other co-reactants for component (A).

Table 9 illustrates the use of vinyl ester and bisphenol A fumarate resin systems for component (A).

Table 10 illustrates the present invention using higher glass content.

Table 11 illustrates the suitability of the present invention for bulk molding compounds.

Table 12 illustrates the properties obtainable when using a supplemental thickening agent. The examples according to the present invention show both improved mechanical and shrinkage properties.

Table 13 illustrates examples of resin systems having good gel formation characteristics wherein acid containing reactants are used for component (A).

                  TABLE I                                                          ______________________________________                                                       Example                                                                        1       2       3                                                ______________________________________                                         Reichhold 31615-20                                                                             100.00                                                         Owens Corning E-903-1     100.00                                               Reichhold 31610                   100.00                                       Styrene Monomer                   10.00                                        BYK Chemie W-996                                                                               2.50      2.50    2.50                                         General Electric AF-9000                                                                       0.02      0.02    0.02                                         Trigonox C      1.25      1.25    1.25                                         Plasticolors SP-9073                                                                           0.20      0.20    0.20                                         Zinc Stearate   5.00      5.00    5.00                                         Camelwite       175.00    175.00  175.00                                       XAMA-7          4.50      5.00    4.75                                         1" Glass Fibers 91.10     91.25   94.33                                        SMC Apparent Viscosity                                                         (10.sup.6 cP) (at log shear rate of                                            1.5(1/sec))                                                                    at 2 days       321       405     454                                          at 14 days      320       434     475                                          at 58 days      289       405     468                                          at 105 days     338       464     447                                          ______________________________________                                    

                                      TABLE II                                     __________________________________________________________________________                Example                                                                        4   5   6   7   8   9   10                                          __________________________________________________________________________     Reichhold 31632                                                                           100.00                                                                             60.00                                                                              100.00                                                                             100.00                                                  Reichhold 31615-20                                                                            40.00       60.00                                               Reichhold 31610                1o0.00                                          Dow Derakane 41 1-45               70.00                                       Dow Derakane 780                   30.00                                       Styrene Monomer                                                                           8.00                                                                               3.00    5.00                                                                               30.00                                                                              10.00                                                                              4.50                                        BF Goodrich Hycar              10.00                                           1300 X-8                                                                       BF Goodrich Hycar                                                                         8.00                                                                1300 X-13                                                                      Ricon Resins   9.00    15.00       13.50                                       131 MA-17                                                                      Union Carbide Neulon                                                                              40.00                                                       T Plus                                                                         Poly(Styrene/Ethylene-     10.00                                               Propylene)                                                                     Diblock Copolymer                                                              BYK Chemie W-996                                                                          2.50                                                                               2.50                                                                               3.00                                                                               2.50                                                                               2.50                                                                               2.50                                                                               2.50                                        General Electric AF-                                                                      0.02                                                                               0.02                                                                               0.02                                                                               0.02                                                                               0.02                                                                               0.02                                                                               0.02                                        9000                                                                           Akzo Trigonox 29-B-75                                                                     1.00                                                                               1.00                                                                               1.00                                                                               1.00                                                    Plasticolors SP-9139                                                                      0.25                                                                               0.25                                                                               0.25                                                                               0.25                                                    Trigonox C                 1.25                                                                               1.25                                                                               1.25                                        Plasticolors SP-9073       0.20                                                                               0.20                                                                               0.20                                        Zinc Stearate                                                                             5.00                                                                               5.00                                                                               5.00                                                                               6.00                                                                               5.00                                                                               6.00                                                                               5.00                                        Camelwite  175.00                                                                             175.00                                                                             150.00                                                                             200.00                                                                             175.00                                                                             150.00                                                                             175.00                                      XAMA-7     0.90                                                                               1.85                                                                               0.23                                                                               3.11                                                                               2.70                                                                               5.40                                                                               2.80                                        1" Glass Fibers                                                                           94.95                                                                              93.99                                                                              94.58                                                                              105.12                                                                             90.53                                                                              90.12                                                                              96.24                                       SMC Apparent Viscosity                                                         (10.sup.6 cP) (at log shear                                                    rate of 1.5 (1/sec))                                                           at 2 days  35  166 56  --  64  263 --                                          at 6 days  55  --  78  --  61  264 --                                          at 14 days 55  244 71  --  59  238 --                                          __________________________________________________________________________

                                      TABLE III                                    __________________________________________________________________________                  Example                                                                        C1  C2  8   11  12  13                                            __________________________________________________________________________     Reichhold 31615-20                                                                          60.00                                                                              60.00                                                                              60.00                                                                              60.00                                                                              60.00                                                                              60.00                                         Styrene Monomer                                                                             30.00                                                                              30.00                                                                              30.00                                                                              30.00                                                                              30.00                                                                              30.00                                         (Styrene/Butadiene/Styrene)                                                                     4.00        4.00                                                                               4.00                                          Block Copolymer                                                                Poly(Styrene/Ethylene-                                                                      10.00                                                                              6.00                                                                               10.00                                                                              10.00                                                                              6.00                                                                               6.00                                          Propylene) Diblock                                                             Copolymer                                                                      BYK Chemie W-996                                                                            2.50                                                                               2.50                                                                               2.50                                                                               2.50                                                                               2.50                                                                               2.50                                          General Electric AF-9000                                                                    0.02                                                                               0.02                                                                               0.02                                                                               0.02                                                                               0.02                                                                               0.02                                          Trigonox C   1.25                                                                               1.25                                                                               1.25                                                                               1.25                                                                               1.25                                                                               1.25                                          Plasticolors SP-9073                                                                        0.20                                                                               0.20                                                                               0.20                                                                               0.20                                                                               0.20                                                                               0.20                                          Zinc Stearate                                                                               5.00                                                                               5.00                                                                               5.00                                                                               5.00                                                                               5.00                                                                               5.00                                          Camelwite    175.00                                                                             175.00                                                                             175.00                                                                             175.00                                                                             175.00                                                                             175.00                                        XAMA-7               2.70                                                                               1.35                                                                               .1.35                                                                              2.70                                          Plasticolors PG-9033                                                                        1.68                                                                               1.68    0.84                                                                               0.84                                              1" Glass Fibers                                                                             90.21                                                                              90.21                                                                              90.53                                                                              90.37                                                                              90.37                                                                              90.53                                         Brookfield Paste Viscosity                                                     (10.sup.3 cP) (TA spindle at 5 or                                              10 rpm)                                                                        initial      19.2                                                                               22.4                                                                               16.0                                                                               20.8                                                                               25.6                                                                               27.2                                          at 10 min    206.4                                                                              534.4                                                                              52.0                                                                               118.4                                                                              232.0                                                                              164.8                                         SMC Apparent Viscosity                                                         (106 cP) (at log shear rate of                                                 1.5 (1/sec))                                                                   at 2 days    101 105 64  98  83  113                                           __________________________________________________________________________

                  TABLE IV                                                         ______________________________________                                         Composition      C3      C4      14    15                                      ______________________________________                                         Reichhold 31615-20                                                                              60.00   60.00   60.00 60.00                                   Union Carbide Neulon T Plus                                                                     40.00           40.00                                         Modified PVA                                                                   Alpha Owens Corning RP-700                                                                              40.00         40.00                                   PMMA                                                                           BYK Chemie W-996 2.50    2.50    2.50  2.50                                    General Electric AF-9000                                                                        0.02    0.02    0.02  0.02                                    Trigonox C       1.25    1.25    1.25  1.25                                    Plasticolors SP-9073                                                                            0.20    0.20    0.20  0.20                                    Zinc Stearate    5.00    5.00    5.00  5.00                                    Camelwite Calcium Carbonate                                                                     175.00  175.00  175.00                                                                               175.00                                  Plasticolors PG-91 146 Mg(OH).sub.2                                                             3.36    3.36                                                  Dispersion                                                                     XAMA-7           2.88    2.88                                                  1" Glass Fibers  90.74   90.74   90.58 90.58                                   SMC Apparent Viscosity (10.sup.6 cP)                                            at log shear rate = 1.5 (1/sec)!                                              2 Days           49      80      81    120                                     6 Days           71      215     86    119                                     14 Days          117     255     85    127                                     30 Days          137     262     87    12                                      ______________________________________                                    

                                      TABLE V                                      __________________________________________________________________________     Composition  16   17   18   19   20   21                                       __________________________________________________________________________     Reichhold 31615-20                                                                          60.00                                                             Alpha Owens Corning E-903                                                                        60.00                                                                               60.00                                                   Reichhold 31610        60.00                                                                               60.00                                              Alpha Owens Corning              60.00                                         E-4381                                                                         Styrene Monomer        26.00                                                                               40.00                                                                               30.00                                                                               30.00                                    Union Carbide Neulon T Plus                                                                 40.00                                                             Modified PVA                                                                   Ashland LP-2035   40.00                                                        Chevron MD-9520        14.00                                                   Polystyrene                                                                    Poly(Styrenel/Ethylene-     10.00                                                                               10.00                                                                               10.00                                    Propylene)                                                                     Diblock Copolymer                                                              BYK Chemie W-996                                                                            2.50 3.00 2.50 2.50 2.50 3.00                                     General Electric AF-9000                                                                    0.02 0.02 0.02 0.02 0.02 0.02                                     Trigonox C   1.25 1.25 1.25 1.25 1.25 1.25                                     Plasticolors SP-9073                                                                        0.20 0.20 0.20 0.20 0.20 0.20                                     Zinc Stearate                                                                               5.00 5.00 5.00 5.00 5.00 5.00                                     Camelwite    175.00                                                                              200.00                                                                              175.00                                                                              150.00                                                                              175.00                                        Aluminum Trihydrate                   175.00                                   Plasticolors PG-9033 MgO                                                                         0.84 0.87                                                    Dispersion                                                                     Plasticolors PG-91 146                                                                      1.68                                                              Mg(OH).sub.2 Dispersion                                                        XAMA-7       1.44 1.50 1.42 2.85 2.34 3.00                                     1 Glass Fibers                                                                              90.66                                                                               98.47                                                                               90.40                                                                               85.84                                                                               90.41                                                                               90.78                                    Tensile Strength (MPa)                                                                      63.1 63.7 55.6 56.1 67.9 55.7                                     Tensile Modulus (MPa)                                                                       10,066                                                                              11,239                                                                              9,722                                                                               9,377                                                                               12,066                                                                              9,377                                    Tensile Elongation (%)                                                                      1.40 0.90 0.90 1.00 1.00 0.80                                     Flexural Strength (MPa)                                                                     148.9                                                                               144.8                                                                               144.5                                                                               142.8                                                                               164.7                                                                               162.0                                    Flexural Modulus (MPa)                                                                      8,619                                                                               9,446                                                                               8,205                                                                               7,860                                                                               9,239                                                                               8,825                                    Linear shrinkage (mils/inch)                                                                0.17 -0.25                                                                               -0.25                                                                               -0.17                                                                               0.50 -0.58                                     expansion positive!                                                           __________________________________________________________________________

                                      TABLE VI                                     __________________________________________________________________________     Composition  22   23   24   25   26   27   28                                  __________________________________________________________________________     Reichhold 31615-20                                                                          60.00          60.00                                                                               60.00     60.00                               Alpha Owens Corning E-903                                                                        60.00                                                                               60.00          60.00                                    Styrene Monomer                                                                             30.00                                                                               30.00                    30.00                               Poly(Styrene/Ethylene-                                                                      10.00                                                                               10.00                    10.00                               Propylene)                                                                     Diblock Copolymer                                                              Ashland LP-2035        40.00                                                   Alpha Owens Corning RP-700  40.00                                              PMMA                                                                           Union Carbide LP-90 PVA          40.00                                                                               40.00                                    BYK Chemie W-996                                                                            2.50 2.50 2.50 2.50 2.50 2.50 2.50                                General Electric AF-9000                                                                    0.02 0.02 0.02 0.02 0.02 0.02 0.02                                Trigonox C   1.25 1.25 1.25 1.25 1.25 1.25 1.25                                Plasticolors SP-9073                                                                        0.20 0.20 0.20 0.20 0.20 0.20 0.20                                Zinc Stearate                                                                               5.00 5.00 5.00 5.00 5.00 5.00 5.00                                Camelwite    175.00                                                                              200.00                                                                              200.00                                                                              175.00                                                                              175.00                                                                              200.00                                                                              175.00                              XAMA-2       3.20 3.40 3.40 3.20 3.20 3.40                                     1" Glass Fibers                                                                             90.69                                                                               98.64                                                                               98.64                                                                               90.69                                                                               90.69                                                                               98.64                                                                               90.78                               Tensile Strength (MPa)                                                                      63.6 68.5 66.8 55.2 60.0 65.8 50.4                                Tensile Modulus (MPa)                                                                       11,101                                                                              10,756                                                                              11,170                                                                              8,756                                                                               9,997                                                                               11,170                                                                              8,756                               Tensile Elongation (%)                                                                      1.40 1.10 1.00 0.80 1.00 1.00 0.90                                Flexural Strength (MPa)                                                                     148.8                                                                               149.7                                                                               146.8                                                                               162.7                                                                               136.6                                                                               174.2                                                                               136.2                               Flexural Modulus (MPa)                                                                      8,481                                                                               8,136                                                                               8,343                                                                               10,066                                                                              7,791                                                                               9,515                                                                               8,136                               Linear shrinkage (mils/inch)                                                                -0.42                                                                               -0.50                                                                               -0.42                                                                               -0.25                                                                               0.00 -0.08                                                                               0.00                                 expansion positive!                                                           __________________________________________________________________________

                                      TABLE VII                                    __________________________________________________________________________     Composition   29   30     31   32                                              __________________________________________________________________________     Aristech MR-13017                                                                            100.00                                                                              100.00 100.00                                               Reichhold 31610                100.00                                          Styrene Monomer                                                                              15.00                                                                               3.33   3.33 10.00                                           BF Goodrich Hycar 1 300-X8                                                                   15.00            10.00                                           Ricon Resins 131 MA-10    10.00                                                Ricon Resins 131 MA-5                                                                        10.00                                                            BYK Chemie W-996                                                                             2.50 2.50   2.50 2.50                                            General Electric AF-9000                                                                     0.02 0.02   0.02 0.02                                            Trigonox C    1.25 1.25   1.25 1.25                                            Plasticolors SP-9073                                                                         0.20 0.20   0.20 0.20                                            Zinc Stearate 6.00 5.00   5.00 5.00                                            Camelwite Calcium Carbonate                                                                  150.00                                                                              175.00 175.00                                               Aluminum Trihydrate            150.00                                          XAMA-7        4.62 3.62   3.62 5.40                                            1" Glass Fibers                                                                              93.03                                                                               95.03  95.03                                                                               89.80                                           Tensile Strength (MPa)                                                                       65.5 82.9   69.4 59.3                                            Tensile Modulus (MPa)                                                                        8,550                                                                               12,962 12,066                                                                              9,170                                           Tensile Elongation (%)                                                                       1.20 1.10   1.10 1.10                                            Flexural Strength (Mpa)                                                                      143.6                                                                               174.2  165.6                                                                               143.2                                           Flexural Modulus (MPa)                                                                       7,171                                                                               9,446  9,860                                                                               7,722                                           Linear shrinkage (mils/inch)                                                                 -0.67                                                                               -1.08  -0.50                                                                               -0.75                                            expansion positive!                                                           __________________________________________________________________________

                                      TABLE VIII                                   __________________________________________________________________________     Composition  4     5     6     33                                              __________________________________________________________________________     Reichhold 31632                                                                             100.00                                                                               60.00 100.00                                                                               60.00                                           Reichhold 31615-20 40.00                                                       Reichhold 31610                40.00                                           Syrene Mononmer                                                                             8.00  3.00        3.00                                            BF Goodrich Hycar 1300-X13                                                                  8.00                                                              Union Carbide Neulon T Plus                                                                             40.00                                                 Modified PVA                                                                   Ricon Resins 131 MA-17                                                                            9.00        9.00                                            BYK Chemie W-996                                                                            2.50  2.50  3.00  2.50                                            General Electric AF-9000                                                                    0.02  0.02  0.02  0.02                                            Trigonox 29B75                                                                              1.00  1.00  1.00  1.00                                            Plasticolors SP-9139                                                                        0.25  0.25  0.25  0.25                                            Zinc Stearate                                                                               5.00  5.00  5.00  5.00                                            Camelwite    175.00                                                                               175.00                                                                               150.00                                                                               175.00                                          XAMA-7       0.90  1.85  0.23  1.90                                            1" Glass Fibers                                                                             94.95 93.99 94.58 94.00                                           Tensile Strength (MPa)                                                                      66.6  60.7  84.9  63.2                                            Tensile Modulus (MPa)                                                                       10,066                                                                               11,721                                                                               11,652                                                                               11,376                                          Tensile Elongation (%)                                                                      1.20  1.20  1.40  1.10                                            Flexural Strength (MPa)                                                                     143.0 146.2 191.2 153.1                                           Flexural Modulus (MPa)                                                                      8,963 10,618                                                                               9,308 10,411                                          Linear shrinkage (mils/inch)                                                                -1.42 -1.08 -1.17 -1.25                                            expansion positive!                                                           __________________________________________________________________________

                                      TABLE IX                                     __________________________________________________________________________     Composition    10      34    35                                                __________________________________________________________________________     Dow Derakane 41 1-45                                                                          70.00                                                           Dow Derakane 470-36    88.00                                                   Dow Derakane 780                                                                              30.00   12.00                                                   Reichhold Atlac 382-ES HMW   50.00                                             Styrene Monomer                                                                               4.50          50.00                                             Ricon Resins 131 MA-17                                                                        13.50                                                           Polyurethane Specialties                                                                              5.51                                                    PCA 6-3                                                                        BYK Chemie W-996                                                                              2.50    2.50  2.50                                              General Electric AF-9000                                                                      0.02    0.02  0.02                                              Trigonox C     1.25                                                            Trigonox 29B75 1.00    1.00                                                    Plasticolors SP-9073                                                                          0.20                                                            Plasticolors SP-91 39                                                                         0.25    0.25                                                    Zinc Stearate  5.00    5.00  5.00                                              Camelwite      175.00  200.00                                                                               175.00                                            XAMA-7         2.80    1.12  2.04                                              1" Glass Fibers                                                                               96.24   99.60 90.26                                             Tensile Strength (MPa)                                                                        70.5    67.2  68.0                                              Tensile Modulus (MPa)                                                                         11,583  7,584 9,515                                             Tensile Elongation (%)                                                                        1.20    1.25  1.15                                              Flexural Strength (MPa)                                                                       185.9   176.8 156.8                                             Flexural Modulus (MPa)                                                                        10,066  9,308 8,343                                             Linear shrinkage (mils/inch)                                                                  -1.83   -1.25 -1.67                                              expansion positive!                                                           __________________________________________________________________________

                                      TABLE X                                      __________________________________________________________________________     Composition      36    37    38    39                                          __________________________________________________________________________     Reichhold 31615-20                                                                              60.00                                                         Alpha Owens Corning E-903                                                                             60.00                                                   Reichhold Atlac 382-ES HMW   50.00 35.00                                       Reichhold Atlac 382-ES             15.00                                       Styrene Monomer  30.00       50.00 50.00                                       Poly(StyrenelEthylene-Propylene)                                                                10.00                                                         Diblock Copolymer                                                              Ashland LP-2035        40.00                                                   BYK Chemie W-996 2.00  2.00  1.00                                              General Electric AF-9000                                                                        0.02  0.02  0.02                                              Trigonox C       1.25  1.25                                                    Trigonox 29B75   1.00  1.00                                                    Plasticolors SP-9073                                                                            0.20  0.20                                                    Plasticolors SP-91 39                                                                           0.25  0.25                                                    Zinc Stearate    5.00  5.00  5.00  5.00                                        Camelwite        150.00                                                                               175.00                                                                               80.00                                             Plasticolors PG-9033 MgO Dispersion                                                             0.84  0.84                                                    XAMA-7           1.35  1.50  2.04  2.08                                        1" Glass Fibers  111.71                                                                               122.49                                                                               174.75                                                                               201.18                                      Tensile Strength (MPa)                                                                          68.6  74.5  126.4 211.5                                       Tensile Modulus (MPa)                                                                           11,032                                                                               12,617                                                                               11,239                                                                               14,203                                      Tensile Flongation (%)                                                                          1.00  1.10  1.40  1.80                                        Flexural Strength (MPa)                                                                         176.8 175.3 253.9 360.7                                       Flexural Modulus (MPa)                                                                          9,722 9,584 11,376                                                                               NA                                          Linear shrinkage (mils/inch)  expansion                                                         -0.50 0.00  -0.83 0.00                                        positive!                                                                      __________________________________________________________________________

                                      TABLE XI                                     __________________________________________________________________________                   Example                                                                        40    41    42    43    44    45                                 __________________________________________________________________________     Aristech MR-14017                                                                            100.00                                                                               100.00                                                     Aristech MR-13017         60.00                                                Reichhold 31615-20              60.00 60.00 60.00                              Styrene Monomer                                                                              10.00 10.00 26.00             30.00                              Poly(Styrene/Ethylene-                      10.00                              Propylene)                                                                     Diblock Copolymer                                                              BF Goodrich Hycar 1300 X-8                                                                         10.00                                                      Alpha Owens Corning                   40.00                                    RP-700 PMMA                                                                    Union Carbide LP-90 PVA         40.00                                          Chevron MD-9520           14.00                                                Polystyrene                                                                    BYK Chemie W-996                                                                             6.00  6.00  4.5   4.5   4.5   4.5                                General Electric AF-9000                                                                     0.03  0.03  0.02  0.02  0.02  0.02                               Trigonox C    1.25  1.25  1.25  1.25  1.25  1.25                               Plasticolors SP-9073                                                                         0.20  0.20  0.20  0.20  0.20  0.20                               Zinc Stearate 8.00  8.00  6.00  6.00  6.00  6.00                               Camelwite     300.00                                                                               300.00                                                                               300.00                                                                               300.00                                                                               300.00                                                                               300.00                             XAMA-7        3.25  4.00  2.17        2.03  1.35                               XAMA-2                          3.20                                           Plasticolors PG-9033                  0.42  0.84                               0.5" Glass Fibers                                                                            75.66 77.56 73.08 73.27 73.13 73.09                              Tensile Strength (MPa)                                                                       36.0  30.5  26.7  22.5  25.4  29.6                               Tensile Modulus (MPa)                                                                        9,653 8,274 11,790                                                                               11,928                                                                               12,549                                                                               16,065                             Tensile Elongation (%)                                                                       0.70  0.60  0.36  0.27  0.20  0.28                               Flexural Strength (MPa)                                                                      88.8  82.0  90.6  77.1  93.9  95.3                               Flexural Modulus (MPa)                                                                       6,205 5,861 8,481 6,964 10,135                                                                               10,066                             Linear Shrinkage (mils/inch)                                                                 -3.75 -0.42 -1.42 0.00  0.00  -0.50                               expansion positive!                                                           __________________________________________________________________________

                                      TABLE XII                                    __________________________________________________________________________     Composition   C1    C4    C5    C6    C7                                       __________________________________________________________________________     Reichhold 31615-20                                                                           60.00 60.00             60.00                                    Alpha Owens Corning E-903 60.00 60.00                                          Styrene Monomer                                                                              30.00       30.00                                                Poly(Styrene/Ethylene-                                                                       10.00       10.00                                                Propylene)                                                                     Diblock Copolymer                                                              Union Carbide LP-90 PVA         40.00                                          Alpha Owens Corning 40.00             40.00                                    RP-700 PMMA                                                                    BYK Chemie W-996                                                                             2.50  2.50  3.00  3.00  2.50                                     General Electric AF-9000                                                                     0.02  0.02  0.02  0.02  0.02                                     Trigonox C    1.25  1.25  1.25  1.25  1.25                                     Plasticolors SP-9073                                                                         0.20  0.20  0.20  0.20  0.20                                     Zinc Stearate 5.00  5.00  5.00  5.00  5.00                                     Camelwite     175.00                                                                               175.00                                                                               200.00                                                                               200.00                                                                               175.00                                   Plasticolors PG-9033 MgO                                                                     1.68  1.68  1.68  1.68                                           Dispersion                                                                     Plasticolors PG-91146                 3.36                                     Mg(OH).sub.2                                                                   XAMA-7                                                                         1" Glass Fibers                                                                              90.21 90.21 98.26 98.26 90.74                                    Tensile Strength (MPa)                                                                       57.4  52.3  62.2  57.1  57.9                                     Tensile Modulus (MPa)                                                                        9,997 10,825                                                                               10,825                                                                               10,135                                                                               9,515                                    Tensile Elongation (%)                                                                       1.10  0.90  1.10  1.10  0.80                                     Flexural Strength (MPa)                                                                      134.6 140.7 159.7 147.2 162.1                                    Flexural Modulus (MPa)                                                                       8,619 9,446 8,756 8,412 10,825                                   Linear shrinkage (mils/inch)                                                                 -0.67 -0.58 -0.92 -0.75 -0.67                                     expansion positive!                                                           __________________________________________________________________________     Composition   11    46    47    48    49                                       __________________________________________________________________________     Reichhold 31615-20                                                                           60.00             60.00 60.00                                    Alpha Owens Corning E-903                                                                          60.00 60.00                                                Styrene Monomer                                                                              30.00 30.00                                                      Poly(Styrene/Ethylene-                                                                       10.00 10.00                                                      Propylene)                                                                     Diblock Copolymer                                                              Union Carbide LP-90 PVA   40.00                                                Alpha Owens Corning             40.00 40.00                                    RP-700 PMMA                                                                    BYK Chemie W-996                                                                             2.50  3.00  3.00  2.50  2.50                                     General Electric AF-9000                                                                     0.02  0.02  0.02  0.02  0.02                                     Trigonox C    1.25  1.25  1.25  1.25  1.25                                     Plasticolors SP-9073                                                                         0.20  0.20  0.20  0.20  0.20                                     Zinc Stearate 5.00  5.00  5.00  5.00  5.00                                     Camelwite     175.00                                                                               200.00                                                                               200.00                                                                               175.00                                                                               175.00                                   Plasticolors PG-9033 MgO                                                                     0.84  0.84  1.26  0.42                                           Dispersion                                                                     Plasticolors PG-91146                 1.68                                     Mg(OH).sub.2                                                                   XAMA-7        1.35  1.50  0.75  2.03  1.44                                     1" Glass Fibers                                                                              90.37 98.47 98.36 90.45 90.66                                    Tensile Strength (MPa)                                                                       69.8  72.8  62.8  64.3  67.5                                     Tensile Modulus (MPa)                                                                        12,411                                                                               13,031                                                                               11,997                                                                               11,514                                                                               12,135                                   Tensile Elongation (%)                                                                       1.20  1.20  1.10  1.00  1.10                                     Flexural Strength (MPa)                                                                      167.1 159.1 156.9 166.3 170.2                                    Flexural Modulus (MPa)                                                                       9,584 9,584 8,619 10,411                                                                               10,963                                   Linear shrinkage (mils/inch)                                                                 -0.58 -0.92 -0.33 -0.08 -0.33                                     expansion positive!                                                           __________________________________________________________________________

                  TABLE XIII                                                       ______________________________________                                         Composition      50     51     52   53   54                                    ______________________________________                                         Shell Epon 828 Epoxy Resin                                                                      85.00  85.00  45.00                                           Ciba-Geigy AroCy L-10 Resin    50.00                                                                               90.00                                      DSM Daron XP-21-102                      100.00                                BF Goodrich Hycar 1300-X13                                                                      15.00                                                         BF Goodrich Hycar 1300-X18                                                                             15.00  5.00 10.00                                      Ricon Resins 131 MA-12                   16.00                                 XAMA-7           1.11   1.35   0.45 0.90 2.40                                  ______________________________________                                    

An advantage of this invention is that compounds can be thickened rapidly to reach a stable viscosity plateau that can be adjusted by formulation. The rate of viscosity increase prior to reaching the plateau can also be controlled. The result is that molding compounds thickened by this method remain soft and pliable and have an extended shelf life. Another advantage is that the thickening reaction occurs at ambient conditions without the need for a catalyst that may promote premature crosslinking. Another advantage is that improved glass wet out is realized due, in part, to viscosity control. Another advantage is that the thickening reaction is not inhibited by the presence of water. Another advantage of this method is that it is a general approach that can be applied to a number of different thermoset resins. This provides a great deal of latitude for the development of sheet molding compounds, bulk molding compounds, thick molding compounds, and the like from thermoset resins that may be unthickenable using prior art practices.

While the invention has been explained in relation to its preferred embodiments, it is to be understood that various modifications thereof will become apparent to those skilled in the art upon reading the specification. Therefore, it is to be understood that the invention disclosed herein is intended to cover such modifications as fall within the scope of the appended claims. 

What is claimed is:
 1. A process for making a thickened thermoset resin composition for molding materials, comprising: mixing(A) a composition comprising a carboxylic acid containing thermoset resin composition, wherein said thermoset resin is a carboxylic acid containing unsaturated polyester resin; and (B) a compound comprising at least two aziridine rings.
 2. The process of claim 1 wherein at least one metal oxide or hydroxide (C) is used in combination with (B), the metal in said oxide or hydroxide being selected from the group consisting of Mg, Ca, Zn, and mixtures of two or more thereof.
 3. The process of claim 1 wherein component (A) further comprises an amine acceptor containing thermoset resin composition.
 4. The process of claim 1 wherein component (B) is at least one selected from the group consisting of a trimethylol propane-tris (beta-(N-aziridinyl) proprionate) and a pentaerythritol-tris-(beta-(aziridinyl) propionate).
 5. A process for making a thickened thermoset composition for molding materials, comprising: mixing(A) a composition comprising a carboxylic acid containing thermoset resin composition, wherein said thermoset resin is a carboxylic acid containing unsaturated polyester resin; and (B) a compound represented by the formula ##STR8## wherein in Formula (B-IV) R¹ is --C₂ H₅ or --CH₂ OH, and R⁵ is a hydrogen or methyl group.
 6. A process for making a thickened thermoset resin composition for molding materials, comprising: mixing(A) a composition comprising a carboxylic acid containing thermoset resin composition, wherein said thermoset resin is a carboxylic acid containing unsaturated polyester resin and the resin composition optionally contains an amine acceptor; (B) at least one compound represented by the formula ##STR9## wherein in Formula (B-I): R¹, R², R³ and R⁴ are independently hydrogen or methyl; R⁵ is hydrogen, a hydrocarbon group or a substituted hydrocarbon group, the substituent on said substituted hydrocarbon group is at least one selected from the group consisting of hydroxy, alkoxy, aziridinyl and ester groups; and n is at least 1; and (C) at least one metal oxide or hydroxide in combination with (B), the metal in said metal hydroxide or hydroxide being selected from the group consisting of Mg, Ca, Zn and mixtures of two or more thereof.
 7. A process for making a thickened thermoset resin composition for molding materials, comprising: mixing(A) a composition comprising a carboxylic acid containing thermoset resin composition and further containing acrylic acid, methacrylic acid, maleic acid or anhydride, succinic anhydride, fumaric acid, phthalic acid or anhydride, isophthalic acid, terephthalic acid, adipic acid, polyadipic anhydride, a fatty acid, or a mixture of two or more thereof, wherein said thermoset resin is a carboxylic acid containing unsaturated polyester resin and the resin composition optionally contains an amine acceptor; and (B) at least one compound represented by the formula ##STR10## wherein in Formula (B-I): R¹, R², R³ and R⁴ are independently hydrogen or methyl; R⁵ is hydrogen, a hydrocarbon group or a substituted hydrocarbon group, the substituent on said substituted hydrocarbon group is at least one selected from the group consisting of hydroxy, alkoxy, aziridinyl and ester groups; and n is at least
 1. 8. A process for making a thickened thermoset resin composition for molding materials, comprising: mixing selected from the group consisting(A) a composition comprising a carboxylic acid containing thermoset resin composition, wherein said thermoset resin is a carboxylic acid containing unsaturated polyester resin; (B) a compound comprising at least two aziridine rings; and (C) at least one metal oxide or hydroxide in combination with (B),the metal in said metal hydroxide or hydroxide being selected from the group consisting of Mg, Ca, Zn and mixtures of two or more thereof. 